| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ISO1183/D |
0.936 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ISO1133 |
3.5 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
38 |
µm |
| 薄膜 |
拉伸模量-1%正割(38µm,吹塑薄膜) |
|
ISO1184 |
300 |
MPa |
| 薄膜 |
TensileStress-MD(Break,38µm,BlownFilm) |
|
ISO527-3 |
55.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,38µm,BlownFilm) |
|
ISO1184 |
600 |
% |
| 薄膜 |
落锤冲击(38µm,吹塑薄膜) |
|
ASTMD1709A |
50 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(38µm,BlownFilm) |
|
ASTMD1922 |
30 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-TD(38µm,吹塑薄膜) |
|
ASTMD1922 |
40 |
g |
| 光学性能 |
Gloss(45°,38.0µm,BlownFilm) |
|
ASTMD2457 |
80 |
|
| 光学性能 |
雾度(38.0µm,吹塑薄膜) |
|
ASTMD1003 |
5.0 |
% |