ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 嵌段共聚注塑 | 外观颜色 | |
| 该料用途 | 注塑级 | ||
| 备注说明 | 注塑级 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水性 | ASTM D-570 | >0.01 | % | |
| 熔体流动速率 | ASTM D-1238 | 30 | g/10min | ||
| 密度 | ASTM D-1505 | 0.91 | g/cm3 | ||
| 物理性能 | 模具收缩率 | KPIC Method | 1.4-1.8 | % | |
| 机械性能 | 拉伸强度 | ASTM D-638 | 250 | kgf/cm2 | |
| 断裂伸长率 | ASTM D-638 | 50 | % | ||
| 弯曲模量 | ASTM D-790 | 14000 | kgf/cm2 | ||
| 洛氏硬度 | ASTM D-785 | 90 | R Scale | ||
| IZOD缺口冲击强度 | ASTM D-256 | 13 | kgfcm/cm | ||
| 电气性能 | 损耗因素 | 1KHz | ASTM D-150 | 2 | 10-4 |
| 介电强度 | ASTM D-149 | 40 | KV/М | ||
| Arc Resistance | ASTM D-495 | 130 | sec | ||
| 介电常数 | 1KHz | ASTM D-150 | 2.3 | ||
| 热性能 | 热传导性 | KPIC Method | 3 | 10-4calcm/cmsec℃ | |
| 比热 | KPIC Method | 0.46 | Ш/g℃ | ||
| 维卡软化点 | ASTM D-1525 | 152 | ℃ | ||
| 热变形温度 | ASTM D-648 | 127 | ℃ | ||
| 其它性能 | Volume Resistivity | ASTM D-257 | 1 | 1017Ω.Н | |