ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 嵌段共聚注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 抗冲击 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 其它性能 | 密度 | ASTM D-1505 | 0.91 | g/cm3 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 2 | g/10min | |
| 吸水性 | ASTM D-570 | >0.01 | % | ||
| 机械性能 | 艾佐德冲击强度（缺口） | ASTM D-256 | 50 | kgfcm/cm | |
| Mold Shrinkage (Linear) | KPIC Method | 1.4～1.8 | % | ||
| 断裂伸长率 | ASTM D-638 | <500 | % | ||
| 弯曲模量 | ASTM D-790 | 12500 | kgf/cm2 | ||
| 洛氏硬度 | ASTM D-785 | 85 | R Scale | ||
| 屈服拉伸强度 | ASTM D-638 | 250 | kgf/cm2 | ||
| 电气性能 | 耗散(损耗)因数 | 1KHz | ASTM D-150 | 2 | 10-4 |
| 体积电阻率 | ASTM D-257 | 1 | 1017Ω.Н | ||
| 介电常数 | 1KHz | ASTM D-150 | 2.3 | ||
| 介电强度（短时间） | ASTM D-14 | 40 | kv/m | ||
| Arc Resistance | ASTM D-495 | 130 | sec | ||
| 热性能 | 比热性 | KPIC Method | 0.46 | Ш/g℃ | |
| Heat Conductivity | KPIC Method | 3 | 10-4calcm/cmsec℃ | ||
| 维卡软化点 | ASTM D-1525 | 152 | ℃ | ||
| 热变形温度 | ASTM D-648 | 100 | ℃ | ||