| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重2 | ASTMD792 | 1.15 | g/cm³ | |
| 物理性能 | 密度3 | DIN53479 | 1.15 | g/cm³ | |
| 物理性能 | 溶化体积流率（MVR）(190°C/5.0kg) | 45.0 | cm³/10min | ||
| 物理性能 | 收缩率-流动(注塑) | InternalMethod | 0.90 | % | |
| 机械性能 | Abrasion2 | DIN53516 | 35 | mm³ | |
| ELASTOMERS | 弹性体 | TestMethod | NominalValue | Unit | |
| ELASTOMERS | TensileStress3(100%Strain,0.635mm) | DIN53504 | 3.40 | MPa | |
| ELASTOMERS | TensileStress3(300%Strain,0.635mm) | DIN53504 | 7.00 | MPa | |
| ELASTOMERS | TensileStress3(Break,0.635mm) | DIN53504 | 35.0 | MPa | |
| ELASTOMERS | TensileElongation3(Break,0.635mm) | DIN53504 | 880 | % | |
| ELASTOMERS | TearStrength3(0.635mm) | DIN53515 | 45 | kN/m | |
| ELASTOMERS | 压缩永久变形2 | 23°C,24hr | ASTMD395 | 34 | % |
| ELASTOMERS | 压缩永久变形2 | 70°C,24hr | ASTMD395 | 48 | % |
| ELASTOMERS | 压缩永久变形2 | 23°C,24hr | DIN53517 | 34 | % |
| ELASTOMERS | 压缩永久变形2 | 70°C,24hr | DIN53517 | 48 | % |
| 硬度 | 肖氏硬度 | 邵氏A,注塑 | ASTMD2240 | 70 | |
| 硬度 | 肖氏硬度 | 邵氏D,注塑 | ASTMD2240 | 20 | |
| 硬度 | 肖氏硬度 | 邵氏A,注塑 | DIN53505 | 71 | |
| 硬度 | 肖氏硬度 | 邵氏D,注塑 | DIN53505 | 21 | |
| 热性能 | TMA3 | High:635.0µm | 165 | °C | |
| 热性能 | TMA3 | Low:635.0µm | InternalMethod | 120 | °C |