| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.949 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.060 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
13 |
µm |
| 薄膜 |
SecantModulus-MD(13µm) |
|
ASTMD882 |
945 |
MPa |
| 薄膜 |
SecantModulus-TD(13µm) |
|
ASTMD882 |
1050 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,13µm) |
|
ASTMD882 |
34.5 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,13µm) |
|
ASTMD882 |
29.0 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,13µm) |
|
ASTMD882 |
84.1 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,13µm) |
|
ASTMD882 |
57.2 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,13µm) |
|
ASTMD882 |
320 |
% |
| 薄膜 |
TensileElongation-TD(Break,13µm) |
|
ASTMD882 |
390 |
% |
| 薄膜 |
DartDropImpact2(13µm) |
|
ASTMD1709 |
340 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(13µm) |
|
ASTMD1922 |
11 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(13µm) |
|
ASTMD1922 |
76 |
g |