| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.945 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
6.0 |
g/10min |
| 物理性能 |
抗环境应力开裂 |
10%Igepal,模压成型,F50 |
ASTMD1693A |
25.0 |
hr |
| 物理性能 |
抗环境应力开裂 |
100%Igepal,模压成型,F50 |
ASTMD1693A |
70.0 |
hr |
| 机械性能 |
TensileStrength3(Yield,3.17mm,RotationalMolded) |
|
ASTMD638 |
20.0 |
MPa |
| 机械性能 |
TensileElongation3(Break,3.17mm,RotationalMolded) |
|
ASTMD638 |
460 |
% |
| 机械性能 |
弯曲模量4 |
2%Secant:3.17mm,RotationalMolded |
ASTMD790 |
740 |
MPa |
| 机械性能 |
弯曲模量4 |
Tangent:3.17mm,RotationalMolded |
ASTMD790 |
910 |
MPa |
| 冲击性能 |
ARMImpact |
-40°C,3.20mm |
|
92.0 |
J |
| 冲击性能 |
ARMImpact |
-40°C,6.35mm |
|
223 |
J |
| 硬度 |
肖氏硬度(邵氏D,模压成型) |
|
ASTMD2240 |
63 |
|
| 热性能 |
DeflectionTemperatureUnderLoad(0.45MPa,Unannealed,3.17mm,RotationalMolded) |
|
ASTMD648 |
64.0 |
°C |
| 热性能 |
DeflectionTemperatureUnderLoad(1.8MPa,Unannealed,3.17mm,RotationalMolded) |
|
ASTMD648 |
44.0 |
°C |
| 热性能 |
脆化温度 |
|
ASTMD746A |
-75.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15255 |
118 |
°C |
| 热性能 |
熔融温度 |
|
|
130 |
°C |
| 热性能 |
结晶峰温度(DSC)12 |
|
ASTMD3418 |
113 |
°C |