| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.04 |
g/cm³ |
| 物理性能 |
MeltMass-FlowRate(MFR)2(220°C/10.0kg) |
|
ASTMD1238 |
21 |
g/10min |
| 物理性能 |
收缩率-流动(注塑) |
|
ASTMD955 |
0.50to0.70 |
% |
| 机械性能 |
TensileStrength3(Yield,23°C,3.18mm,InjectionMolded) |
|
ASTMD638 |
41.5 |
MPa |
| 机械性能 |
FlexuralModulus-Tangent4(23°C,3.18mm,InjectionMolded) |
|
ASTMD790 |
2630 |
MPa |
| 机械性能 |
FlexuralStrength4(23°C,3.18mm,InjectionMolded) |
|
ASTMD790 |
72.5 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.18mm,注塑) |
|
ASTMD256 |
120 |
J/m |
| 热性能 |
载荷下热变形温度 |
1.8MPa,未退火,3.18mm,注塑 |
ASTMD648 |
81.1 |
°C |
| 热性能 |
载荷下热变形温度 |
1.8MPa,未退火,6.35mm,注塑 |
ASTMD648 |
90.0 |
°C |