| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.918 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
8.3 |
g/10min |
| 薄膜 |
TensileStrength-MD(Break,70µm,BlownFilm) |
|
ASTMD882 |
25.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,70µm,BlownFilm) |
|
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,70µm,BlownFilm) |
|
ASTMD882 |
380 |
% |
| 薄膜 |
TensileElongation-TD(Break,70µm,BlownFilm) |
|
ASTMD882 |
870 |
% |
| 薄膜 |
FlexuralModulus-1%Secant,MD(70µm,BlownFilm) |
|
ASTMD790 |
70.0 |
MPa |
| 薄膜 |
落锤冲击(70µm,吹塑薄膜) |
|
ASTMD1709 |
70 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-TD(70µm,吹塑薄膜) |
|
ASTMD1922 |
56 |
g |
| 光学性能 |
光泽度(60°,70.0µm,吹塑薄膜) |
|
ASTMD2457 |
76 |
|
| 光学性能 |
雾度(70.0µm,吹塑薄膜) |
|
ASTMD1003 |
8.0 |
% |