| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
1.0 |
g/10min |
| 物理性能 |
醋酸乙烯含量 |
|
|
4.0 |
wt% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
32 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(32µm) |
|
ASTMD882 |
145 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(32µm) |
|
ASTMD882 |
165 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,32µm) |
|
ASTMD882 |
25.5 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,32µm) |
|
ASTMD882 |
21.4 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,32µm) |
|
ASTMD882 |
340 |
% |
| 薄膜 |
TensileElongation-TD(Break,32µm) |
|
ASTMD882 |
500 |
% |
| 薄膜 |
落锤冲击(32µm) |
|
ASTMD1709 |
170 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD(32µm) |
|
ASTMD1922 |
180 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(32µm) |
|
ASTMD1922 |
250 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
95.0 |
°C |
| 光学性能 |
光泽度(45°,31.8µm) |
|
ASTMD2457 |
75 |
|
| 光学性能 |
雾度(31.8µm) |
|
ASTMD1003 |
4.0 |
% |