| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.922 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.27 |
g/10min |
| 薄膜 |
SecantModulus-2%Secant,MD(70µm,BlownFilm) |
|
ASTMD882 |
140 |
MPa |
| 薄膜 |
SecantModulus-2%Secant,TD(70µm,BlownFilm) |
|
ASTMD882 |
150 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,70µm,BlownFilm) |
|
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,70µm,BlownFilm) |
|
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,70µm,BlownFilm) |
|
ASTMD882 |
380 |
% |
| 薄膜 |
TensileElongation-TD(Break,70µm,BlownFilm) |
|
ASTMD882 |
910 |
% |
| 薄膜 |
落锤冲击(70µm,吹塑薄膜) |
|
ASTMD1709 |
230 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(70µm,BlownFilm) |
|
ASTMD1922 |
300 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-TD(70µm,吹塑薄膜) |
|
ASTMD1922 |
220 |
g |
| 光学性能 |
光泽度 |
45°,70.0µm,BlownFilm |
ASTMD2457 |
39 |
|
| 光学性能 |
光泽度 |
60°,70.0µm,BlownFilm |
ASTMD2457 |
49 |
|
| 光学性能 |
雾度(70.0µm,吹塑薄膜) |
|
ASTMD1003 |
20 |
% |