| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.921 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.25 |
g/10min |
| 物理性能 |
醋酸乙烯含量 |
|
|
1.5 |
wt% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
51 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(51µm) |
|
ASTMD882 |
152 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(51µm) |
|
ASTMD882 |
179 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,51µm) |
|
ASTMD882 |
20.7 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,51µm) |
|
ASTMD882 |
19.3 |
MPa |
| 薄膜 |
伸长率-MD(断裂,50µm) |
|
ASTMD882 |
320 |
% |
| 薄膜 |
TensileElongation-TD(Break,51µm) |
|
ASTMD882 |
500 |
% |
| 薄膜 |
落锤冲击(50µm) |
|
ASTMD1709 |
230 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD(50µm) |
|
ASTMD1922 |
190 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(51µm) |
|
ASTMD1922 |
240 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
91.0 |
°C |