ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 低摩擦系数,均聚物,食品接触的合规性,清晰度，高,抗撞击性，良好,光滑性 薄膜挤出,吹塑薄膜,流延薄膜 | 外观颜色 | |
| 该料用途 | 薄膜,流延薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.924 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 3.0 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | 32 | µm | ||
| 薄膜 | SecantModulus-1%Secant,MD | 32µm,BlownFilm | ASTMD882 | 159 | MPa |
| 薄膜 | SecantModulus-1%Secant,MD | 32µm,CastFilm | ASTMD882 | 208 | MPa |
| 薄膜 | SecantModulus-1%Secant,TD | 32µm,BlownFilm | ASTMD882 | 172 | MPa |
| 薄膜 | SecantModulus-1%Secant,TD | 32µm,CastFilm | ASTMD882 | 197 | MPa |
| 薄膜 | 抗张强度-MD | Yield,32µm,BlownFilm | ASTMD882 | 10.9 | MPa |
| 薄膜 | 抗张强度-MD | Yield,32µm,CastFilm | ASTMD882 | 9.38 | MPa |
| 薄膜 | TensileStrength-TD | Yield,32µm,BlownFilm | ASTMD882 | 10.7 | MPa |
| 薄膜 | TensileStrength-TD | Yield,32µm,CastFilm | ASTMD882 | 9.31 | MPa |
| 薄膜 | 抗张强度-MD | Break,32µm,BlownFilm | ASTMD882 | 18.6 | MPa |
| 薄膜 | 抗张强度-MD | Break,32µm,CastFilm | ASTMD882 | 29.1 | MPa |
| 薄膜 | TensileStrength-TD | Break,32µm,BlownFilm | ASTMD882 | 17.2 | MPa |
| 薄膜 | TensileStrength-TD | Break,32µm,CastFilm | ASTMD882 | 17.0 | MPa |
| 薄膜 | 伸长率-MD | Break,32µm,BlownFilm | ASTMD882 | 200 | % |
| 薄膜 | 伸长率-MD | Break,32µm,CastFilm | ASTMD882 | 230 | % |
| 薄膜 | TensileElongation-TD | Break,32µm,BlownFilm | ASTMD882 | 500 | % |
| 薄膜 | TensileElongation-TD | Break,32µm,CastFilm | ASTMD882 | 610 | % |
| 薄膜 | 落锤冲击 | 32µm,BlownFilm | ASTMD1709 | 65 | g |
| 薄膜 | 落锤冲击 | 32µm,CastFilm | ASTMD1709 | 110 | g |
| 薄膜 | 埃尔曼多夫抗撕强度-MD | 32µm,BlownFilm | ASTMD1922 | 270 | g |
| 薄膜 | 埃尔曼多夫抗撕强度-MD | 32µm,CastFilm | ASTMD1922 | 300 | g |
| 薄膜 | ElmendorfTearStrength-TD | 32µm,BlownFilm | ASTMD1922 | 170 | g |
| 薄膜 | ElmendorfTearStrength-TD | 32µm,CastFilm | ASTMD1922 | 160 | g |
| 光学性能 | 光泽度 | 45°,31.8µm,BlownFilm | ASTMD2457 | 70 | |
| 光学性能 | 光泽度 | 45°,31.8µm,CastFilm | ASTMD2457 | 77 | |
| 光学性能 | 雾度 | 31.8µm,BlownFilm | ASTMD1003 | 5.4 | % |
| 光学性能 | 雾度 | 31.8µm,铸造薄膜 | ASTMD1003 | 3.4 | % |