| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.920 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.25 |
g/10min |
| 机械性能 |
抗张强度(屈服) |
|
ASTMD638 |
9.79 |
MPa |
| 机械性能 |
抗张强度(断裂) |
|
ASTMD638 |
17.9 |
MPa |
| 机械性能 |
伸长率(屈服) |
|
ASTMD638 |
100 |
% |
| 机械性能 |
伸长率(断裂) |
|
ASTMD638 |
700 |
% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
51 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(51µm) |
|
ASTMD882 |
207 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(51µm) |
|
ASTMD882 |
241 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,51µm) |
|
ASTMD882 |
20.7 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,51µm) |
|
ASTMD882 |
19.0 |
MPa |
| 薄膜 |
伸长率-MD(断裂,50µm) |
|
ASTMD882 |
310 |
% |
| 薄膜 |
TensileElongation-TD(Break,51µm) |
|
ASTMD882 |
430 |
% |
| 薄膜 |
落锤冲击(50µm) |
|
ASTMD1709 |
180 |
g |
| 硬度 |
肖氏硬度(邵氏D) |
|
ASTMD2240 |
45 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-75.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
93.0 |
°C |