| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD4883 |
0.921 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
2.5 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
38 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(38µm,BlownFilm) |
|
ASTMD882 |
186 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(38µm,BlownFilm) |
|
ASTMD882 |
220 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,38µm,BlownFilm) |
|
ASTMD882 |
26.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,38µm,BlownFilm) |
|
ASTMD882 |
19.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,38µm,BlownFilm) |
|
ASTMD882 |
250 |
% |
| 薄膜 |
TensileElongation-TD(Break,38µm,BlownFilm) |
|
ASTMD882 |
750 |
% |
| 薄膜 |
落锤冲击(38µm,吹塑薄膜) |
|
ASTMD1709A |
100 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
94.0 |
°C |
| 光学性能 |
光泽度(45°,38.0µm,吹塑薄膜) |
|
ASTMD2457 |
70 |
|
| 光学性能 |
Haze(38.1µm,BlownFilm) |
|
ASTMD1003 |
6.0 |
% |