| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.920 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
1.0 |
g/10min |
| 机械性能 |
TensileStrength2(1.91mm) |
|
ASTMD638 |
14.5 |
MPa |
| 机械性能 |
TensileElongation2(Break,1.91mm) |
|
ASTMD638 |
660 |
% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
32 |
µm |
| 薄膜 |
SecantModulus-MD(BlownFilm) |
|
ASTME111 |
200 |
MPa |
| 薄膜 |
SecantModulus-TD(BlownFilm) |
|
ASTME111 |
234 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,32µm,BlownFilm) |
|
ASTMD882 |
24.1 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,32µm,BlownFilm) |
|
ASTMD882 |
16.5 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,32µm,BlownFilm) |
|
ASTMD882 |
200 |
% |
| 薄膜 |
TensileElongation-TD(Break,32µm,BlownFilm) |
|
ASTMD882 |
500 |
% |
| 薄膜 |
落锤冲击(32µm,吹塑薄膜) |
|
ASTMD1709 |
120 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(32µm,BlownFilm) |
|
ASTMD1922 |
300 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(32µm,BlownFilm) |
|
ASTMD1922 |
130 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
92.0 |
°C |