| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.922 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.50 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
51 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(51µm) |
|
ASTMD882 |
186 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(51µm) |
|
ASTMD882 |
205 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,51µm) |
|
ASTMD882 |
12.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,51µm) |
|
ASTMD882 |
12.0 |
MPa |
| 薄膜 |
抗张强度-MD(断裂,50µm) |
|
ASTMD882 |
31.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,51µm) |
|
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
伸长率-MD(断裂,50µm) |
|
ASTMD882 |
200 |
% |
| 薄膜 |
TensileElongation-TD(Break,51µm) |
|
ASTMD882 |
300 |
% |
| 薄膜 |
DartDropImpact2(51µm) |
|
ASTMD1709A |
170 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD(50µm) |
|
ASTMD1922 |
140 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(51µm) |
|
ASTMD1922 |
130 |
g |