| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.958 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.45 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD2(25µm,BlownFilm) |
|
ASTMD882A |
1050 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD2(25µm,BlownFilm) |
|
ASTMD882A |
1370 |
MPa |
| 薄膜 |
TensileStrength-MD3(Yield,25µm,BlownFilm) |
|
ASTMD882A |
31.0 |
MPa |
| 薄膜 |
TensileStrength-TD3(Yield,25µm,BlownFilm) |
|
ASTMD882A |
17.9 |
MPa |
| 薄膜 |
TensileStrength-MD3(Break,25µm,BlownFilm) |
|
ASTMD882A |
53.1 |
MPa |
| 薄膜 |
TensileStrength-TD3(Break,25µm,BlownFilm) |
|
ASTMD882A |
17.9 |
MPa |
| 薄膜 |
TensileElongation-MD3(Break,25µm,BlownFilm) |
|
ASTMD882A |
270 |
% |
| 薄膜 |
TensileElongation-TD3(Break,25µm,BlownFilm) |
|
ASTMD882A |
<10 |
% |
| 薄膜 |
落锤冲击(25µm,吹塑薄膜) |
|
ASTMD1709A |
<50 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(25µm,BlownFilm) |
|
ASTMD1922 |
15 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(25µm,BlownFilm) |
|
ASTMD1922 |
1100 |
g |
| 薄膜 |
WaterVaporTransmissionRate(38°C,25µm,BlownFilm) |
|
ASTMF1249 |
11 |
g/m²/24hr |