| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.962 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/2.16kg |
ASTMD1238 |
2.0 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/21.6kg |
ASTMD1238 |
55 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
割线模量 |
1%正割,MD:25µm,吹塑薄膜 |
ASTMD882 |
862 |
MPa |
| 薄膜 |
割线模量 |
2%Secant,MD:25µm,BlownFilm |
ASTMD882 |
689 |
MPa |
| 薄膜 |
割线模量 |
1%正割,TD:25µm,吹塑薄膜 |
ASTMD882 |
883 |
MPa |
| 薄膜 |
割线模量 |
2%Secant,TD:25µm,BlownFilm |
ASTMD882 |
703 |
MPa |
| 薄膜 |
TensileStrength-MD2(Yield,25µm,BlownFilm) |
|
ASTMD882A |
26.2 |
MPa |
| 薄膜 |
TensileStrength-TD2(Yield,25µm,BlownFilm) |
|
ASTMD882A |
27.6 |
MPa |
| 薄膜 |
TensileStrength-MD2(Break,25µm,BlownFilm) |
|
ASTMD882A |
51.7 |
MPa |
| 薄膜 |
TensileStrength-TD2(Break,25µm,BlownFilm) |
|
ASTMD882A |
23.4 |
MPa |
| 薄膜 |
TensileElongation-MD2(Break,25µm,BlownFilm) |
|
ASTMD882A |
700 |
% |
| 薄膜 |
TensileElongation-TD2(Break,25µm,BlownFilm) |
|
ASTMD882A |
700 |
% |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
25µm,吹塑薄膜 |
ASTMD1922 |
24 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
51µm,CoextrudedFilm |
ASTMD1922 |
70 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
25µm,吹塑薄膜 |
ASTMD1922 |
390 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
51µm,CoextrudedFilm |
ASTMD1922 |
500 |
g |
| 薄膜 |
水气透过率 |
38°C,25µm,BlownFilm |
ASTMF1249 |
3.9 |
g/m²/24hr |
| 薄膜 |
水气透过率 |
38°C,51µm,CoextrudedFilm |
ASTMF1249 |
2.9 |
g/m²/24hr |