| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.949 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.40 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(25µm,BlownFilm) |
|
ASTMD882 |
638 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(25µm,BlownFilm) |
|
ASTMD882 |
769 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,25µm,BlownFilm) |
|
ASTMD882 |
22.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,25µm,BlownFilm) |
|
ASTMD882 |
24.0 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,25µm,BlownFilm) |
|
ASTMD882 |
35.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,25µm,BlownFilm) |
|
ASTMD882 |
33.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,25µm,BlownFilm) |
|
ASTMD882 |
530 |
% |
| 薄膜 |
TensileElongation-TD(Break,25µm,BlownFilm) |
|
ASTMD882 |
890 |
% |
| 薄膜 |
落锤冲击(25µm,吹塑薄膜) |
|
ASTMD1709A |
70 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(25µm,BlownFilm) |
|
ASTMD1922 |
13 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(25µm,BlownFilm) |
|
ASTMD1922 |
480 |
g |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
LowFrictionPuncture-BlownFilm(25.0µm) |
|
|
570 |
J/cm |