| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD792 |
0.941 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
3.5 |
g/10min |
| 物理性能 |
抗环境应力开裂 |
50°C,100%Igepal,模压成型,F50 |
ASTMD1693A |
>1000 |
hr |
| 物理性能 |
抗环境应力开裂 |
50°C,100%Igepal,模压成型,F50 |
ASTMD1693B |
>1000 |
hr |
| 机械性能 |
TensileStrength4(Yield,1.90mm,CompressionMolded) |
|
ASTMD638 |
20.2 |
MPa |
| 机械性能 |
TensileElongation4(Yield,1.90mm,CompressionMolded) |
|
ASTMD638 |
12 |
% |
| 机械性能 |
弯曲模量-1%正割(模压成型) |
|
ASTMD790 |
827 |
MPa |
| 冲击性能 |
ARMImpact-RotationalMolded |
-40°C,3.17mm |
ARM |
95.0 |
J |
| 冲击性能 |
ARMImpact-RotationalMolded |
-40°C,6.35mm |
ARM |
230 |
J |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火,模压成型) |
|
ASTMD648 |
62.0 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火,模压成型) |
|
ASTMD648 |
43.0 |
°C |
| 热性能 |
熔融温度 |
|
DSC |
126 |
°C |
| 可燃性 |
UL阻燃等级 |
|
UL94 |
HB |
|