| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.950 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
<0.10 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
12 |
µm |
| 薄膜 |
TensileStrength-MD(Yield,12µm) |
|
ASTMD882 |
26.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,12µm) |
|
ASTMD882 |
14.0 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,12µm) |
|
ASTMD882 |
61.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,12µm) |
|
ASTMD882 |
27.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,12µm) |
|
ASTMD882 |
300 |
% |
| 薄膜 |
TensileElongation-TD(Break,12µm) |
|
ASTMD882 |
410 |
% |
| 薄膜 |
DartDropImpact2(12µm) |
|
ASTMD1709A |
200 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(12µm) |
|
ASTMD1922 |
15 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(12µm) |
|
ASTMD1922 |
25 |
g |
| 热性能 |
熔融温度 |
|
ASTMD3417 |
130 |
°C |