ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D792 | 1.41 | |||
| 吸水率 | ASTM D570 | 0.22 | % | |||
| 成型收缩率 | ASTM D955 | 2.0 | % | |||
| 机械性能 | 拉伸强度 | ASTM D638 | 630 | kg/cm2 | ||
| 拉伸率 | ASTM D638 | 40 | % | |||
| 弯曲强度 | ASTM D790 | 920 | kg/cm2 | |||
| 弯曲弹性率 | ASTM D790 | 26000 | kg/cm2 | |||
| Izod缺口冲击强度 | ASTM D256 | 6.0 | Kg/cm.cm | |||
| 洛氏硬度 | ASTM D785 | 80 | M | |||
| 电气性能 | 表面电阻率 | ASTM D257 | 1×1013 | Ω.cm | ||
| 体积电阻率 | ASTM D257 | 1×1012 | Ω | |||
| 绝缘破坏强度 | ASTM D149 | 19 | KV/mm | |||
| 介电常数 | ASTM D150 | 3.7 | ||||
| 介电损耗正切 | ASTM D150 | 0.006 | ||||
| 热性能 | 熔融指数 | ASTM D1238 | 30 | g/10min | ||
| 熔点 | ASTM D1525 | 166 | ℃ | |||
| 热变形温度 | - | 0.45MPa | ASTM D648 | 160 | ℃ | |
| - | 1.82MPa | ASTM D648 | 110 | ℃ | ||
| 阻燃性 | UL94 | HB | ||||
| 线膨胀系数 | ASTM D696 | 11-13 | ||||