ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 1.13 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(235°C/1.0kg) | ASTMD1238 | 4.5 | g/10min | |
| 物理性能 | 吸水率 | 24hr | ASTMD570 | 1.6 | % |
| 物理性能 | 吸水率 | 饱和 | ASTMD570 | 9.5 | % |
| 物理性能 | 吸水率 | 平衡 | ASTMD570 | 2.7 | % |
| 物理性能 | MoistureContent | ASTMD6869 | >800 | ppm | |
| 物理性能 | [email protected]%SulfuricAcid | 3.01 | |||
| 物理性能 | 粘度-FAV | ASTMD789 | 73.0 | ||
| 薄膜 | 薄膜厚度-经测试 | 51 | µm | ||
| 薄膜 | 弹性模量-MD2 | ASTMD882 | 710 | MPa | |
| 薄膜 | 弹性模量-TD2 | ASTMD882 | 620 | MPa | |
| 薄膜 | 抗张强度2 | MD:屈服 | ASTMD882 | 40.0 | MPa |
| 薄膜 | 抗张强度2 | TD:屈服 | ASTMD882 | 30.0 | MPa |
| 薄膜 | 抗张强度2 | MD:断裂 | ASTMD882 | 90.0 | MPa |
| 薄膜 | 抗张强度2 | TD:断裂 | ASTMD882 | 90.0 | MPa |
| 薄膜 | 伸长率2 | MD:断裂 | ASTMD882 | 340 | % |
| 薄膜 | 伸长率2 | TD:断裂 | ASTMD882 | 360 | % |
| 薄膜 | 二氧化碳传输速率(23°C) | ASTMD1434 | 72.8 | cm³/m²/24hr | |
| 薄膜 | 氮传输速率(23°C) | ASTMD1434 | 14.0 | cm³/m²/24hr | |
| 薄膜 | 氧气传输速率(23°C) | ASTMD3985 | 40 | cm³/m²/24hr | |
| 薄膜 | 水气透过率(38°C,100%RH) | ASTMF1249 | 990 | g·mm/m²/atm/24hr | |
| 薄膜 | ElmendorfTearStrength | MD:23°C | ASTMD1922 | 590 | N |
| 薄膜 | ElmendorfTearStrength | TD:23°C | ASTMD1922 | 530 | N |
| 薄膜 | GravesTear | MD:23°C | ASTMD1004 | 3530 | N |
| 薄膜 | GravesTear | TD:23°C | ASTMD1004 | 3290 | N |
| 薄膜 | 薄膜厚度-经测试 | 51 | µm | ||
| 薄膜 | 弹性模量-MD2 | ASTMD882 | 710 | MPa | |
| 薄膜 | 弹性模量-TD2 | ASTMD882 | 620 | MPa | |
| 薄膜 | 抗张强度2 | MD:屈服 | ASTMD882 | 40.0 | MPa |
| 薄膜 | 抗张强度2 | TD:屈服 | ASTMD882 | 30.0 | MPa |
| 薄膜 | 抗张强度2 | MD:断裂 | ASTMD882 | 90.0 | MPa |
| 薄膜 | 抗张强度2 | TD:断裂 | ASTMD882 | 90.0 | MPa |
| 薄膜 | 伸长率2 | MD:断裂 | ASTMD882 | 340 | % |
| 薄膜 | 伸长率2 | TD:断裂 | ASTMD882 | 360 | % |
| 薄膜 | 二氧化碳传输速率(23°C) | ASTMD1434 | 72.8 | cm³/m²/24hr | |
| 薄膜 | 氮传输速率(23°C) | ASTMD1434 | 14.0 | cm³/m²/24hr | |
| 薄膜 | 氧气传输速率(23°C) | ASTMD3985 | 40 | cm³/m²/24hr | |
| 薄膜 | 水气透过率(38°C,100%RH) | ASTMF1249 | 990 | g·mm/m²/atm/24hr | |
| 薄膜 | ElmendorfTearStrength | MD:23°C | ASTMD1922 | 590 | N |
| 薄膜 | ElmendorfTearStrength | TD:23°C | ASTMD1922 | 530 | N |
| 薄膜 | GravesTear | MD:23°C | ASTMD1004 | 3530 | N |
| 薄膜 | GravesTear | TD:23°C | ASTMD1004 | 3290 | N |
| 热性能 | 熔融温度 | 220 | °C | ||
| 补充信息 | PunctureIndex3(23°C) | 193.4 | kN/m | ||
| 补充信息 | PunctureResistance3(23°C) | 1000 | g | ||