ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 光学 其它 其它 | 外观颜色 | |
| 该料用途 | 光盘 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 流动系数 | 300℃,1.2kg | ASTM D1238 | 48 | g/10min | |
| 比重 | 23/23℃ | ASTM D792 | 1.20 | |||
| 吸水率 | 24hr,23℃ | ASTM D570 | 0.20 | % | ||
| 成型收缩率 | - | Parallel | ASTM D955 | 0.5-0.7 | % | |
| - | across | ASTM D955 | 0.5-0.7 | % | ||
| 机械性能 | 曲折率 | ASTM D542 | 1.585 | |||
| 降伏引张强度 | 23℃ | ASTM D638 | 630 | % | ||
| 延伸率 | 降伏点 | 23℃ | ASTM D638 | 6 | % | |
| 破断点 | 23℃ | ASTM D638 | 70 | % | ||
| 弯曲强度 | 23℃ | ASTM D790 | 920 | kg/cm2 | ||
| 弯曲模量 | 23℃ | ASTM D790 | 24000 | kg/cm2 | ||
| 洛氏硬度 | ASTM D785 | M-77 | M | |||
| 电气性能 | 体积电阻率 | ASTM D257 | 3 | ×1016Ω•cm | ||
| 热性能 | 线膨胀系数 | 40-100℃ | ASTM D696 | 6-8 | ×105cm/cm/℃ | |
| 热传导率 | ASTM C177 | 0.2 | W/m℃ | |||
| 光学性能 | 全光穿透率 | 3mm厚 | ASTM D1003 | 89 | % | |
| 浊度 | 3.2mm厚 | ASTM D1003 | <0.8 | % | ||