ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| Physical | 比重 | ASTMD792 | 1.11 | g/cm³ | |
| Physical | 表观密度 | ASTMD1895 | 0.65 | g/cm³ | |
| Physical | 熔流率（熔体流动速率）(230°C/5.0kg) | ASTMD1238 | 6.5 | g/10min | |
| Physical | 收缩率-流动 | ASTMD955 | 0.40to0.60 | % | |
| Physical | 吸水率(饱和) | ASTMD570 | 0.30 | % | |
| Mechanical | 拉伸模量 | ASTMD638 | 2960 | MPa | |
| Mechanical | 抗张强度 | ASTMD638 | 43.4 | MPa | |
| Mechanical | 伸长率(屈服) | ASTMD638 | 3.6 | % | |
| Mechanical | 伸长率(断裂) | ASTMD638 | 6.7 | % | |
| Mechanical | 弯曲模量 | ASTMD790 | 2280 | MPa | |
| Mechanical | 弯曲强度 | ASTMD790 | 74.5 | MPa | |
| Impact | 悬壁梁缺口冲击强度 | 0°C,6.35mm | ASTMD256 | 43 | J/m |
| Impact | 悬壁梁缺口冲击强度 | 23°C,6.35mm | ASTMD256 | 110 | J/m |
| Hardness | 洛氏硬度(M级) | ASTMD785 | 30 | ||
| Thermal | 载荷下热变形温度(1.8MPa,退火,6.35mm) | ASTMD648 | 72.8 | °C | |
| Thermal | 维卡软化温度 | ASTMD1525 | 98.9 | °C | |
| Thermal | 线形热膨胀系数-流动(0到100°C) | ASTMD696 | 7.2E-5 | cm/cm/°C | |
| Optical | 透射率(3200µm) | ASTMD1003 | 89.0 | % | |
| Optical | 雾度(3200µm) | ASTMD1003 | 3.0 | % | |
| Optical | 黄度指数(3.20mm) | InternalMethod | -0.30 | YI | |