| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.75to1.80 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
30to40 |
g/10min |
| 物理性能 |
吸水率(23°C,24hr) |
|
ASTMD570 |
<0.040 |
% |
| 物理性能 |
MoldShrinkage-Linear |
|
|
2.0to3.0 |
% |
| 机械性能 |
TensileModulus2,3(23°C,2.00mm) |
|
ASTMD638 |
1800to2600 |
MPa |
| 机械性能 |
TensileStrength4(Yield,23°C,2.00mm) |
|
ASTMD638 |
50.0to60.0 |
MPa |
| 机械性能 |
TensileStrength4(Break,23°C,2.00mm) |
|
ASTMD638 |
30.0to50.0 |
MPa |
| 机械性能 |
TensileElongation4(Yield,23°C,2.00mm) |
|
ASTMD638 |
5.0to10 |
% |
| 机械性能 |
TensileElongation4(Break,23°C,2.00mm) |
|
ASTMD638 |
20to300 |
% |
| 机械性能 |
TaberAbrasionResistance(1000Cycles,1000g,CS-10Wheel) |
|
ASTMD4060 |
5.00to10.0 |
mg |
| 机械性能 |
摩擦系数 |
Dynamic |
ASTMD1894 |
0.15to0.35 |
|
| 机械性能 |
摩擦系数 |
Static |
ASTMD1894 |
0.20to0.40 |
|
| 冲击性能 |
CharpyNotchedImpactStrength-2m/s(23°C,4.00mm) |
|
ASTMD6110 |
25.0to75.0 |
J/m |
| 硬度 |
ShoreHardness(ShoreD,1sec,2.00mm) |
|
ASTMD2240 |
73to80 |
|
| 热性能 |
玻璃转化温度 |
|
ASTMD4065 |
-40.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15255 |
135to145 |
°C |
| 热性能 |
熔融温度 |
|
ASTMD3418 |
170to175 |
°C |
| 热性能 |
结晶峰温度(DSC)12 |
|
ASTMD3418 |
134to144 |
°C |
| 热性能 |
CLTE-Flow(0to40°C) |
|
ASTMD696 |
1.4E-4 |
cm/cm/°C |
| 热性能 |
比热 |
23°C |
ASTME968 |
1200 |
J/kg/°C |
| 热性能 |
比热 |
100°C |
ASTME968 |
1600 |
J/kg/°C |
| 热性能 |
导热系数(23°C) |
|
ASTMC177 |
0.20 |
W/m/K |
| 热性能 |
结晶热 |
|
ASTMD3417 |
54.0to60.0 |
J/g |
| 热性能 |
结晶点 |
|
ASTMD3418 |
137to144 |
°C |
| 热性能 |
融合热量 |
|
ASTMD3417 |
58.0to67.0 |
J/g |
| 电气性能 |
表面电阻率 |
|
ASTMD257 |
>1.0E+14 |
ohms |
| 电气性能 |
体积电阻率 |
|
ASTMD257 |
>1.0E+14 |
ohms·cm |
| 电气性能 |
介电强度(23°C) |
|
ASTMD149 |
20to25 |
kV/mm |
| 电气性能 |
DielectricConstant(23°C,1.00mm,1kHz) |
|
ASTMD150 |
7.00to10.0 |
|
| 可燃性 |
UL阻燃等级(0.100mm) |
|
UL94 |
V-0 |
|
| 可燃性 |
OxygenIndex6(3.00mm) |
|
ASTMD2863 |
44 |
% |