| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.75to1.80 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/5.0kg) |
|
ASTMD1238 |
3.0to9.0 |
g/10min |
| 物理性能 |
吸水率(23°C,24hr) |
|
ASTMD570 |
<0.040 |
% |
| 机械性能 |
拉伸模量2(23°C,2.00mm) |
|
ASTMD638 |
360to480 |
MPa |
| 机械性能 |
TensileStrength3(Yield,23°C,2.00mm) |
|
ASTMD638 |
15.0to18.0 |
MPa |
| 机械性能 |
TensileStrength3(Break,23°C,2.00mm) |
|
ASTMD638 |
20.0to40.0 |
MPa |
| 机械性能 |
TensileElongation3(Yield,23°C,2.00mm) |
|
ASTMD638 |
12to15 |
% |
| 机械性能 |
TensileElongation3(Break,23°C,2.00mm) |
|
ASTMD638 |
600to750 |
% |
| 热性能 |
玻璃转化温度 |
|
ASTMD4065 |
-40.0 |
°C |
| 热性能 |
熔融温度 |
|
ASTMD3418 |
130to136 |
°C |
| 热性能 |
结晶峰温度(DSC)12 |
|
ASTMD3418 |
89.0to93.0 |
°C |
| 热性能 |
结晶热 |
|
ASTMD3417 |
20.0to24.0 |
J/g |
| 热性能 |
融合热量 |
|
ASTMD3417 |
20.0to24.0 |
J/g |
| 电气性能 |
表面电阻率 |
|
ASTMD257 |
>1.0E+14 |
ohms |
| 电气性能 |
体积电阻率 |
|
ASTMD257 |
>1.0E+14 |
ohms·cm |