| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.75to1.80 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/10.0kg) |
|
ASTMD1238 |
2.5to4.0 |
g/10min |
| 物理性能 |
收缩率-流动 |
|
|
2.0to3.0 |
% |
| 物理性能 |
吸水率(23°C,24hr) |
|
ASTMD570 |
<0.040 |
% |
| 机械性能 |
拉伸模量2(23°C,2.00mm) |
|
ASTMD638 |
1250to1400 |
MPa |
| 机械性能 |
TensileStrength3(Yield,23°C,2.00mm) |
|
ASTMD638 |
34.0to40.0 |
MPa |
| 机械性能 |
TensileStrength3(Break,23°C,2.00mm) |
|
ASTMD638 |
34.0to40.0 |
MPa |
| 机械性能 |
TensileElongation3(Yield,23°C,2.00mm) |
|
ASTMD638 |
9.0to12 |
% |
| 机械性能 |
TensileElongation3(Break,23°C,2.00mm) |
|
ASTMD638 |
100to300 |
% |
| 机械性能 |
摩擦系数 |
与自身-动态 |
ASTMD1894 |
0.20to0.30 |
|
| 机械性能 |
摩擦系数 |
与自身-静态 |
ASTMD1894 |
0.20to0.40 |
|
| 机械性能 |
TaberAbrasionResistance(1000Cycles,1000g,CS-10Wheel) |
|
ASTMD4060 |
5.00to10.0 |
mg |
| 冲击性能 |
NotchedIzodImpact4(23°C,4.00mm) |
|
ASTMD6110 |
1000 |
J/m |
| 硬度 |
DurometerHardness(ShoreD,2.00mm) |
|
ASTMD2240 |
70 |
|
| 热性能 |
玻璃转化温度 |
|
ASTMD4065 |
-40.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15255 |
167 |
°C |
| 热性能 |
熔融温度 |
|
ASTMD3418 |
170to174 |
°C |
| 热性能 |
结晶峰温度(DSC)12 |
|
ASTMD3418 |
142to146 |
°C |
| 热性能 |
CLTE-Flow(0to40°C) |
|
ASTMD696 |
1.3E-4to1.8E-4 |
cm/cm/°C |
| 热性能 |
比热 |
23°C |
ASTME968 |
1200 |
J/kg/°C |
| 热性能 |
比热 |
100°C |
ASTME968 |
1600 |
J/kg/°C |
| 热性能 |
导热系数(23°C) |
|
ASTMC177 |
0.20 |
W/m/K |
| 热性能 |
结晶热 |
|
ASTMD3417 |
42.0to50.0 |
J/g |
| 热性能 |
融合热量 |
|
ASTMD3417 |
41.0to50.0 |
J/g |
| 电气性能 |
表面电阻率 |
|
ASTMD257 |
>1.0E+14 |
ohms |
| 电气性能 |
体积电阻率 |
|
ASTMD257 |
>1.0E+14 |
ohms·cm |