| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ISO1183 |
1.80to1.82 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/10.0kg) |
|
ASTMD1238 |
2.0to4.5 |
g/10min |
| 物理性能 |
吸水率(23°C,24hr) |
|
ISO62 |
<0.040 |
% |
| 机械性能 |
TensileModulus2(23°C,1.50mm) |
|
ASTMD638 |
1100to1350 |
MPa |
| 机械性能 |
TensileStrength3(Yield,23°C,1.50mm) |
|
ASTMD638 |
30.0to40.0 |
MPa |
| 机械性能 |
TensileStrength3(Break,23°C,1.50mm) |
|
ASTMD638 |
30.0to40.0 |
MPa |
| 机械性能 |
TensileElongation3(Yield,23°C,1.50mm) |
|
ASTMD638 |
8.0to12 |
% |
| 机械性能 |
TensileElongation3(Break,23°C,1.50mm) |
|
ASTMD638 |
50to300 |
% |
| 机械性能 |
摩擦系数 |
与自身-动态 |
ASTMD1894 |
0.10to0.20 |
|
| 机械性能 |
摩擦系数 |
与自身-静态 |
ASTMD1894 |
0.050to0.20 |
|
| 机械性能 |
TaberAbrasionResistance(1000Cycles,1000g,CS-10Wheel) |
|
ASTMD4060 |
5.00to10.0 |
mg |
| 热性能 |
熔融温度 |
|
ASTMD3418 |
170to174 |
°C |
| 热性能 |
结晶峰温度(DSC)12 |
|
ASTMD3418 |
144to148 |
°C |
| 热性能 |
结晶热 |
|
ASTMD3417 |
38.0to48.0 |
J/g |
| 热性能 |
HeatofFusion-(80°Ctoendofmelting) |
|
ASTMD3417 |
41.0to50.0 |
J/g |