ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 抗低温冲击 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D792 | 1.14 | |||
| 成型收缩率 | ASTM D955 | 0.5-0.8 | % | |||
| 机械性能 | 拉伸强度 | - | ASTM D638 | 560 | kg/cm2 | |
| - | ASTM D638 | 55 | MPa | |||
| - | ASTM D638 | 7960 | psi | |||
| 断裂伸长率 | ASTM D638 | ＞100 | % | |||
| 弯曲强度 | - | ASTM D790 | 770 | kg/cm2 | ||
| - | ASTM D790 | 76 | MPa | |||
| - | ASTM D790 | 10900 | psi | |||
| 弯曲模量 | - | ASTM D790 | 22000 | kg/cm2 | ||
| - | ASTM D790 | 1960 | MPa | |||
| - | ASTM D790 | 285 | psi | |||
| Izod缺口冲击强度 | - | ASTM D256 | 65 | Kg.cm/cm | ||
| - | ASTM D256 | 635 | J/m | |||
| - | ASTM D256 | 12.0 | ft.ib/in | |||
| 洛氏硬度 | ASTM D785 | 109 | R | |||
| 热性能 | 熔融指数 | 3 | g/10min | |||
| 热变形温度 | - | 1.82MPa | ASTM D648 | 113 | ℃ | |
| - | 1.82MPa | ASTM D648 | 235 | ℉ | ||