| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ISO1183 |
0.930to0.990 |
g/cm³ |
| 机械性能 |
WearResistance2 |
|
ASTMD3844 |
Noappreciablelossofgrain,textureorcolor |
|
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress-AcrossFlow3(100%Strain) |
|
ISO37 |
1.20 |
MPa |
| ELASTOMERS |
TensileStress-AcrossFlow3(Yield) |
|
ISO37 |
3.50 |
MPa |
| ELASTOMERS |
TensileElongation-AcrossFlow3(Break) |
|
ISO37 |
530 |
% |
| ELASTOMERS |
TearStrength-AcrossFlow4 |
|
ISO34-1 |
20 |
kN/m |
| ELASTOMERS |
压缩永久变形 |
23°C,22hr |
ASTMD395B |
14 |
% |
| ELASTOMERS |
压缩永久变形 |
100°C,22hr |
ASTMD395B |
33 |
% |
| ELASTOMERS |
压缩永久变形4 |
23°C,22hr |
ISO815 |
14 |
% |
| ELASTOMERS |
压缩永久变形4 |
100°C,22hr |
ISO815 |
33 |
% |
| 硬度 |
肖氏硬度(邵氏A,15秒) |
|
ISO868 |
41to47 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-54.0 |
°C |
| 热性能 |
BrittlenessTemperature(TypeB) |
|
ISO812 |
-54.0 |
°C |
| 老化 |
ChangeinTensileStrengthinAir(110°C,1000hr) |
|
ISO188 |
-10 |
% |
| 老化 |
ChangeinTensileStrainatBreakinAir(110°C,1000hr) |
|
ISO188 |
-18 |
% |
| 老化 |
ChangeinShoreHardnessinAir(ShoreA,110°C,1000hr) |
|
ISO188 |
2.0 |
|
| 老化 |
ChangeinTensileProperties-Stressat100%ElongationinAir,1000hrs(110°C) |
|
ISO188 |
12 |
% |
| 可燃性 |
燃烧速率 |
|
ISO3795 |
15 |
mm/min |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
FadeResistance6 |
|
|
DeltaE<3 |
|