| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.958 |
g/cm³ |
| 物理性能 |
密度 |
|
ISO1183 |
0.960 |
g/cm³ |
| 物理性能 |
DetergentResistance |
|
UL2157 |
f4 |
|
| 物理性能 |
DetergentResistance |
|
UL749 |
f3 |
|
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
拉伸应力-横向流量(100%应变,23°C) |
|
ASTMD412 |
7.10 |
MPa |
| ELASTOMERS |
拉伸应力-横向流量(100%应变,23°C) |
|
ISO37 |
7.10 |
MPa |
| ELASTOMERS |
抗张强度-横向流量(断裂,23°C) |
|
ASTMD412 |
15.0 |
MPa |
| ELASTOMERS |
TensileStress-AcrossFlow(Break,23°C) |
|
ISO37 |
15.0 |
MPa |
| ELASTOMERS |
伸长率-横向流量(断裂,23°C) |
|
ASTMD412 |
580 |
% |
| ELASTOMERS |
伸长率-横向流量(断裂,23°C) |
|
ISO37 |
580 |
% |
| ELASTOMERS |
撕裂强度-横向流量2(23°C) |
|
ASTMD624 |
54.0 |
kN/m |
| ELASTOMERS |
TearStrength-AcrossFlow3(23°C) |
|
ISO34-1 |
54 |
kN/m |
| ELASTOMERS |
CompressionSet4 |
70°C,22hr |
ASTMD395B |
36 |
% |
| ELASTOMERS |
CompressionSet4 |
125°C,70hr |
ASTMD395B |
44 |
% |
| ELASTOMERS |
压缩永久变形4 |
70°C,22hr |
ISO815 |
36 |
% |
| ELASTOMERS |
压缩永久变形4 |
125°C,70hr |
ISO815 |
44 |
% |
| 硬度 |
肖氏硬度(邵氏A,15秒,23°C) |
|
ISO868 |
93 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-54.0 |
°C |
| 热性能 |
脆化温度 |
|
ISO812 |
-54.0 |
°C |
| 热性能 |
RTIElec |
|
UL746 |
100 |
°C |
| 热性能 |
RTIStr |
1.0mm |
UL746 |
90.0 |
°C |
| 热性能 |
RTIStr |
1.5mm |
UL746 |
90.0 |
°C |
| 热性能 |
RTIStr |
3.0mm |
UL746 |
95.0 |
°C |
| 老化 |
空气中拉伸强度的变化率(150°C,168hr) |
|
ASTMD573 |
-15 |
% |
| 老化 |
空气中拉伸强度的变化率(150°C,168hr) |
|
ISO188 |
-15 |
% |
| 老化 |
空气中极限伸长率的变化率(150°C,168hr) |
|
ASTMD573 |
-16 |
% |
| 老化 |
ChangeinTensileStrainatBreakinAir(150°C,168hr) |
|
ISO188 |
-16 |
% |
| 老化 |
ChangeinDurometerHardnessinAir(ShoreA,150°C,168hr) |
|
ASTMD573 |
2.0 |
|
| 老化 |
ChangeinShoreHardnessinAir(ShoreA,150°C,168hr) |
|
ISO188 |
2.0 |
|
| 老化 |
ChangeinTensileStrength(125°C,70hr,inIRM903Oil) |
|
ASTMD471 |
-29 |
% |
| 老化 |
ChangeinTensileStress(125°C,70hr,inIRM903Oil) |
|
ISO1817 |
-29 |
% |
| 老化 |
ChangeinUltimateElongation(125°C,70hr,inIRM903Oil) |
|
ASTMD471 |
-32 |
% |
| 老化 |
ChangeinTensileStrainatBreak(125°C,70hr,inIRM903Oil) |
|
ISO1817 |
-32 |
% |
| 老化 |
体积变化(125°C,70hr,在IRM903油中) |
|
ASTMD471 |
48 |
% |
| 老化 |
体积变化(125°C,70hr,在IRM903油中) |
|
ISO1817 |
48 |
% |
| 老化 |
ContinuousUpperTemperatureResistance(1008hr) |
|
SAEJ2236 |
135 |
°C |
| 电气性能 |
DielectricStrength(23°C,2.00mm) |
|
ASTMD149 |
32 |
kV/mm |
| 电气性能 |
DielectricConstant(23°C,1.98mm) |
|
ASTMD150 |
2.40 |
|
| 电气性能 |
DielectricConstant(23°C,1.98mm) |
|
IEC60250 |
2.40 |
|
| 电气性能 |
相比耐漏电起痕指数(CTI) |
|
UL746 |
PLC0 |
|
| 电气性能 |
高电弧燃烧指数(HAI) |
|
UL746 |
PLC0 |
|
| 电气性能 |
高压电弧抗点燃指数(HVAR)(PLC) |
|
UL746 |
PLC5 |
|
| 电气性能 |
高电压电弧起痕速率(HVTR) |
|
UL746 |
PLC1 |
|
| 电气性能 |
热丝引燃(HWI) |
1.0mm |
UL746 |
PLC4 |
|
| 电气性能 |
热丝引燃(HWI) |
1.5mm |
UL746 |
PLC3 |
|
| 电气性能 |
热丝引燃(HWI) |
3.0mm |
UL746 |
PLC2 |
|
| 可燃性 |
UL阻燃等级 |
1.0mm |
UL94 |
HB |
|
| 可燃性 |
UL阻燃等级 |
1.5mm |
UL94 |
HB |
|
| 可燃性 |
UL阻燃等级 |
3.0mm |
UL94 |
HB |
|