| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ISO1183 |
0.920to0.980 |
g/cm³ |
| 机械性能 |
WearResistance2 |
|
ASTMD3844 |
Noappreciablelossofgrain,textureorcolor |
|
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress-AcrossFlow3(100%Strain) |
|
ISO37 |
1.30 |
MPa |
| ELASTOMERS |
TensileStress-AcrossFlow3(Yield) |
|
ISO37 |
3.20 |
MPa |
| ELASTOMERS |
TensileElongation-AcrossFlow3(Break) |
|
ISO37 |
430 |
% |
| ELASTOMERS |
TearStrength-AcrossFlow4 |
|
ISO34-1 |
19 |
kN/m |
| ELASTOMERS |
压缩永久变形 |
70°C,22hr |
ASTMD395B |
30 |
% |
| ELASTOMERS |
压缩永久变形 |
125°C,70hr |
ASTMD395B |
20 |
% |
| ELASTOMERS |
压缩永久变形4 |
70°C,22hr |
ISO815 |
30 |
% |
| ELASTOMERS |
压缩永久变形4 |
125°C,70hr |
ISO815 |
20 |
% |
| 硬度 |
肖氏硬度(邵氏A,15秒) |
|
ISO868 |
41to47 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-56.0 |
°C |
| 热性能 |
BrittlenessTemperature(TypeB) |
|
ISO812 |
-56.0 |
°C |
| 老化 |
ChangeinTensileStrengthinAir(135°C,1000hr) |
|
ISO188 |
-20to10 |
% |
| 老化 |
ChangeinTensileStrainatBreakinAir(135°C,1000hr) |
|
ISO188 |
-25to10 |
% |
| 老化 |
ChangeinShoreHardnessinAir(ShoreA,135°C,1000hr) |
|
ISO188 |
-3.0to3.0 |
|
| 老化 |
ChangeinTensileProperties-Stressat100%ElongationinAir,1000hrs(135°C) |
|
ISO188 |
-12to12 |
% |
| 可燃性 |
燃烧速率 |
|
ISO3795 |
15 |
mm/min |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
ColorFastness-toLight6 |
|
|
DeltaE<3.0 |
|