| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.924 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
2.0 |
g/10min |
| 机械性能 |
TensileStrength2(Break,0.0318mm) |
|
ASTMD638 |
23.0 |
MPa |
| 薄膜 |
FilmThickness-Recommended/Available3 |
|
|
<1.0mil(25µ) |
|
| 薄膜 |
弹性模量-MD |
|
ASTMD882 |
164 |
MPa |
| 薄膜 |
弹性模量-TD |
|
ASTMD882 |
188 |
MPa |
| 薄膜 |
TensileStrength-MD2(Yield,32µm) |
|
ASTMD882 |
10.0 |
MPa |
| 薄膜 |
TensileStrength-TD2(Yield,32µm) |
|
ASTMD882 |
9.50 |
MPa |
| 薄膜 |
TensileStrength-MD2(Break,32µm) |
|
ASTMD882 |
23.0 |
MPa |
| 薄膜 |
TensileStrength-TD2(Break,32µm) |
|
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
TensileElongation-MD2(Break,32µm) |
|
ASTMD882 |
230 |
% |
| 薄膜 |
TensileElongation-TD2(Break,32µm) |
|
ASTMD882 |
580 |
% |
| 薄膜 |
DartDropImpact4(32µm) |
|
ASTMD1709A |
140 |
g |
| 薄膜 |
ElmendorfTearStrength-MD2(32µm) |
|
ASTMD1922 |
240 |
g |
| 薄膜 |
ElmendorfTearStrength-TD2(32µm) |
|
ASTMD1922 |
140 |
g |
| 热性能 |
熔融温度 |
|
|
175to185 |
°C |
| 光学性能 |
Gloss2(45°,31.8µm) |
|
ASTMD2457 |
75 |
|
| 光学性能 |
雾度5 |
|
ASTMD1003 |
6.0 |
% |