| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.28 |
g/cm³ |
| 物理性能 |
ESCR |
Antifreeze(Prestone),50%,24hr:23°C |
|
Passed |
|
| 物理性能 |
ESCR |
Antifreeze(Prestone),50%,24hr:100°C |
|
Passed |
|
| 物理性能 |
ESCR |
Gasoline-Unleaded,24hr:23°C |
|
Passed |
|
| 物理性能 |
ESCR |
MotorOil10W-40,24hr:23°C |
|
Passed |
|
| 物理性能 |
ESCR |
MotorOil10W-40,24hr:100°C |
|
Passed |
|
| 物理性能 |
ESCR |
PowerSteeringFluid,24hr:23°C |
|
Passed |
|
| 物理性能 |
ESCR |
PowerSteeringFluid,24hr:100°C |
|
Passed |
|
| 物理性能 |
ESCR |
TransmissionFluid,24hr:23°C |
|
Passed |
|
| 物理性能 |
ESCR |
TransmissionFluid,24hr:100°C |
|
Passed |
|
| 物理性能 |
ESCR |
WindshieldWasherFluid,50%,24hr:23°C |
|
Passed |
|
| 物理性能 |
ESCR |
Thickness-LayerCapability |
|
254.0到330.2 |
µm |
| 硬度 |
洛氏硬度(M级) |
|
ASTMD785 |
86 |
|
| 机械性能 |
拉伸模量3(3.18mm) |
|
ASTMD638 |
2070 |
MPa |
| 机械性能 |
抗张强度3(3.18mm) |
|
ASTMD638 |
55.2 |
MPa |
| 机械性能 |
伸长率3(断裂,3.18mm) |
|
ASTMD638 |
3.0 |
% |
| 机械性能 |
弯曲模量4 |
|
ASTMD790 |
2210 |
MPa |
| 机械性能 |
弯曲强度4 |
|
ASTMD790 |
110 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C) |
|
ASTMD256A |
59 |
J/m |
| 冲击性能 |
无缺口悬臂梁冲击(23°C) |
|
ASTMD256 |
170 |
J/m |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
189 |
°C |
| 热性能 |
玻璃转化温度 |
|
DMA |
230 |
°C |
| 热性能 |
线形热膨胀系数-流动 |
|
ASTMD696 |
5.6E-5 |
cm/cm/°C |
| 电气性能 |
介电强度5,6 |
|
ASTMD149 |
3.1到11 |
kV/mm |
| 电气性能 |
介电常数6 |
|
ASTMD150 |
3.00到3.20 |
|
| 电气性能 |
耗散因数6 |
|
ASTMD150 |
1.1E-3到1.5E-3 |
|
| 电气性能 |
VolumeResistance6 |
|
ASTMD257 |
5.0E+13到1.5E+14 |
ohms |
| 可燃性 |
UL阻燃等级 |
|
UL94 |
V-0 |
|